| Material name | Main product name | Molar ratio | Impurity (wt%) | Purity (%) | Usage examples | |
|---|---|---|---|---|---|---|
| Barium Titanate | BT-S | Ba/Ti 1.00 |
SrO <1.00 |
Nb₂O₅ <0.20 |
>98.0 | General Ceramic Capacitors (High dielectric constant) |
| BT-HP9DX | Ba/Ti 1.00 |
SrO <0.02 |
Nb₂O₅ <0.01 |
>99.8 | Multilayer Ceramic Capacitors (High dielectric constant) |
|
| Strontium Titanate | ST | Sr/Ti 1.00 |
BaO <1.50 |
Nb₂O₅ <0.20 |
>98.0 | General Ceramic Capacitors |
| ST-H100 | Sr/Ti 1.00 |
BaO <0.01 |
Nb₂O₅ <0.01 |
>99.8 | ||
| Calcium Titanate | CT | Ca/Ti 1.00 |
MgO <0.20 |
Nb₂O₅ <0.20 |
>98.0 | |
| Magnesium Titanate | MT-1S | Mg/Ti 1.00 |
SiO₂ <0.20 |
Nb₂O₅ <0.20 |
>98.0 | |
| MT-2 | Mg/Ti 2.00 |
SiO₂ <0.20 |
Nb₂O₅ <0.20 |
>98.0 | ||
| Zinc Titanate | ZT-1 | Zn/Ti 1.00 |
SrO <1.00 |
Nb₂O₅ <0.20 |
>98.0 | |
| Lanthanum Titanate | TLT (La₂Ti₂O₇） |
(La+Nd)/Ti 1.00 |
- | Nb₂O₅ <0.20 |
>98.0 | |
| Neodymium Titanate | TNT (Nd₂Ti₂O₇) |
Nd/Ti 1.00 |
La₂O₃ <0.20 |
Nb₂O₅ <0.20 |
>98.0 | |
| Material name | Main product name | Molar ratio | Impurity (wt%) | Purity (%) | Usage examples | |
|---|---|---|---|---|---|---|
| Barium Zirconate | BZ | Ba/Zr 1.00 |
SrO <1.00 |
SiO₂ <0.30 |
>98.0 | General Ceramic Capacitors (for electrical property adjustment) |
| Calcium Zirconate | CZ | Ca/Zr 1.00 |
MgO <0.20 |
SiO₂ <0.40 |
>98.0 | |
| Material name | Main product name | Molar ratio | Impurity (wt%) | Purity (%) | Usage examples | |
|---|---|---|---|---|---|---|
| Barium Stannate | BS | Ba/Sn 1.00 |
SrO <1.00 |
SiO₂ <0.20 |
>98.0 | General Ceramic Capacitors (for electrical property adjustment) |
| Calcium Stannate | CS | Ca/Sn 1.00 |
MgO <0.20 |
SiO₂ <0.20 |
>98.0 | |
| Material name | Main product name | Molar ratio | Impurity (wt%) | Purity (%) | Usage examples | |
|---|---|---|---|---|---|---|
| Magnesium Silicate | MSI-B | Mg/Si 2.00 |
Al₂O₃ <2.00 |
CaO <1.50 |
>96.0 | Various substrate, Insulators, Capacitors(low dielectric constant) |